PAROC Pro Lock 100

PAROC Pro Lock 100 is a non-combustible stone wool pipe section for industrial pipe lines with z-lock in radial and longitudinal joints. When insulating pipes with these pipe sections you don't need to use any gladding bearing metal structures, which cause remarkable heat bridges.

Datasheet

Updated 21 Jun 2018

General

Certification Number

0809-CPR-1016 / Eurofins Expert Services Ltd, Kivimiehentie 4, FI-02150 Espoo. Finland

Designation Code

MW-EN 14303-T8/T9-ST(+)640-WS1-CL10

Nominal Density

100 kg/m³

Depth of the z-joint is 50 mm.

PAROC stone wool products are capable of withstanding high temperatures. The binder starts to evaporate when its temperature exceeds approximately 200°C. The insulating properties remain unchanged, but the compressive stress weakens. The softening temperature of stone wool products is over 1000°C.

Dimensions

Dimensions
Thickness	Inner Diameter	Pipe Section Length
80 - 160 mm	219 - 914 mm	1200 mm
In accordance with EN 13467	In accordance with EN 13467	In accordance with EN 13467

Dimensional Stability
Property	Value	According to
Maximum Service Temperature - Dimensional Stability	640 °C	EN 14303:2009+A1:2013 (EN 14707)

T8 for outer diameter < 150 mm, T9 for outer diameter ≥ 150 mm

Packaging

Package Type

Cartons or plastic packs on pallet

Properties

Fire Properties

Reaction to Fire
Property	Value	According to
Reaction to Fire, Euroclass	A1_L	EN 14303:2009+A1:2013 (EN 13501-1)

Thermal Properties

Thermal Resistance
Property	Value	According to
Thermal Conductivity in 50 °C, λ₅₀	0,039 W/mK	EN 14303:2009+A1:2013 (EN ISO 8497)
Thermal Conductivity in 100 °C, λ₁₀₀	0,045 W/mK	EN 14303:2009+A1:2013 (EN ISO 8497)
Thermal Conductivity in 200 °C, λ₂₀₀	0.064 W/mK	EN 14303:2009+A1:2013 (EN ISO 8497)
Thermal Conductivity in 300 °C, λ₃₀₀	0.092 W/mK	EN 14303:2009+A1:2013 (EN ISO 8497)
Dimensions and Tolerances	T8 for outer diameter < 150 mm, T9 for outer diameter ≥ 150 mm	EN 14303:2009+A1:2013

Moisture Properties

Water Permeability
Property	Value	According to
Water Absorption, Short Term WS, W_p	≤ 1 kg/m²	EN 14303:2009+A1:2013 (EN 13472)

Rate of Release of Corrosive Substances

Trace Quantities of Water Soluble Ions and the pH Value
Property	Value	According to
Chloride Ions, Cl-	< 10 ppm	EN 14303:2009+A1:2013 (EN 13468)

Durability

Durability of Reaction to Fire Against Ageing/Degradation

The fire performance of mineral wool does not deteriorate with time. The Euroclass classification of product is related to the organic content, which cannot increase with time.

Durability of Reaction to Fire Against High Temperature

The fire performance of mineral wool does not deteriorate with high temperature. The Euroclass classification of the product is related to the organic content, which remains constant or decreases with high temperature.

Durability of Thermal Resistance Against Ageing/Degradation

Thermal conductivity of mineral wool products does not change with time, experience has shown the fibre structure to be stable and the porosity contains no other gases than atmospheric air.

Durability of Thermal Resistance Against High Temperature

Thermal conductivity of mineral wool products does not change with time, experience has shown the fibre structure to be stable and the porosity contains no other gases than atmospheric air.

General
Properties

Certification Number

0809-CPR-1016 / Eurofins Expert Services Ltd, Kivimiehentie 4, FI-02150 Espoo. Finland

Designation Code

MW-EN 14303-T8/T9-ST(+)640-WS1-CL10

Nominal Density

100 kg/m³

Depth of the z-joint is 50 mm.

Dimensions

Dimensions
Thickness	Inner Diameter	Pipe Section Length
80 - 160 mm	219 - 914 mm	1200 mm
In accordance with EN 13467	In accordance with EN 13467	In accordance with EN 13467

Dimensional Stability
Property	Value	According to
Maximum Service Temperature - Dimensional Stability	640 °C	EN 14303:2009+A1:2013 (EN 14707)

T8 for outer diameter < 150 mm, T9 for outer diameter ≥ 150 mm

Packaging

Package Type

Cartons or plastic packs on pallet

Fire Properties

Reaction to Fire
Property	Value	According to
Reaction to Fire, Euroclass	A1_L	EN 14303:2009+A1:2013 (EN 13501-1)

Thermal Properties

Thermal Resistance
Property	Value	According to
Thermal Conductivity in 50 °C, λ₅₀	0,039 W/mK	EN 14303:2009+A1:2013 (EN ISO 8497)
Thermal Conductivity in 100 °C, λ₁₀₀	0,045 W/mK	EN 14303:2009+A1:2013 (EN ISO 8497)
Thermal Conductivity in 200 °C, λ₂₀₀	0.064 W/mK	EN 14303:2009+A1:2013 (EN ISO 8497)
Thermal Conductivity in 300 °C, λ₃₀₀	0.092 W/mK	EN 14303:2009+A1:2013 (EN ISO 8497)
Dimensions and Tolerances	T8 for outer diameter < 150 mm, T9 for outer diameter ≥ 150 mm	EN 14303:2009+A1:2013

Moisture Properties

Water Permeability
Property	Value	According to
Water Absorption, Short Term WS, W_p	≤ 1 kg/m²	EN 14303:2009+A1:2013 (EN 13472)

Rate of Release of Corrosive Substances

Trace Quantities of Water Soluble Ions and the pH Value
Property	Value	According to
Chloride Ions, Cl-	< 10 ppm	EN 14303:2009+A1:2013 (EN 13468)

Durability

Durability of Reaction to Fire Against Ageing/Degradation

The fire performance of mineral wool does not deteriorate with time. The Euroclass classification of product is related to the organic content, which cannot increase with time.

Durability of Reaction to Fire Against High Temperature

Durability of Thermal Resistance Against Ageing/Degradation

Thermal conductivity of mineral wool products does not change with time, experience has shown the fibre structure to be stable and the porosity contains no other gases than atmospheric air.

Durability of Thermal Resistance Against High Temperature

Thermal conductivity of mineral wool products does not change with time, experience has shown the fibre structure to be stable and the porosity contains no other gases than atmospheric air.

Certification Number

0809-CPR-1016 / Eurofins Expert Services Ltd, Kivimiehentie 4, FI-02150 Espoo. Finland

Designation Code

MW-EN 14303-T8/T9-ST(+)640-WS1-CL10

Nominal Density

100 kg/m³

Depth of the z-joint is 50 mm.

Dimensions

Dimensions
Thickness	Inner Diameter	Pipe Section Length
80 - 160 mm	219 - 914 mm	1200 mm
In accordance with EN 13467	In accordance with EN 13467	In accordance with EN 13467

Dimensional Stability
Property	Value	According to
Maximum Service Temperature - Dimensional Stability	640 °C	EN 14303:2009+A1:2013 (EN 14707)

T8 for outer diameter < 150 mm, T9 for outer diameter ≥ 150 mm

Packaging

Package Type

Cartons or plastic packs on pallet

Fire Properties

Reaction to Fire
Property	Value	According to
Reaction to Fire, Euroclass	A1_L	EN 14303:2009+A1:2013 (EN 13501-1)

Thermal Properties

Thermal Resistance
Property	Value	According to
Thermal Conductivity in 50 °C, λ₅₀	0,039 W/mK	EN 14303:2009+A1:2013 (EN ISO 8497)
Thermal Conductivity in 100 °C, λ₁₀₀	0,045 W/mK	EN 14303:2009+A1:2013 (EN ISO 8497)
Thermal Conductivity in 200 °C, λ₂₀₀	0.064 W/mK	EN 14303:2009+A1:2013 (EN ISO 8497)
Thermal Conductivity in 300 °C, λ₃₀₀	0.092 W/mK	EN 14303:2009+A1:2013 (EN ISO 8497)
Dimensions and Tolerances	T8 for outer diameter < 150 mm, T9 for outer diameter ≥ 150 mm	EN 14303:2009+A1:2013

Moisture Properties

Water Permeability
Property	Value	According to
Water Absorption, Short Term WS, W_p	≤ 1 kg/m²	EN 14303:2009+A1:2013 (EN 13472)

Rate of Release of Corrosive Substances

Trace Quantities of Water Soluble Ions and the pH Value
Property	Value	According to
Chloride Ions, Cl-	< 10 ppm	EN 14303:2009+A1:2013 (EN 13468)

Durability

Durability of Reaction to Fire Against Ageing/Degradation

The fire performance of mineral wool does not deteriorate with time. The Euroclass classification of product is related to the organic content, which cannot increase with time.

Durability of Reaction to Fire Against High Temperature

Durability of Thermal Resistance Against Ageing/Degradation

Thermal conductivity of mineral wool products does not change with time, experience has shown the fibre structure to be stable and the porosity contains no other gases than atmospheric air.

Durability of Thermal Resistance Against High Temperature

Thermal conductivity of mineral wool products does not change with time, experience has shown the fibre structure to be stable and the porosity contains no other gases than atmospheric air.